特性級別 | 標準級||| |
牌號 | 1013NB |
加工級別 | 注墮級|||涂覆級||| |
品名 | PA6 1013NB 日本宇部 |
廠家(產地) | 日本宇部 |
用途級別 | 通用級||| |
PA6 1013NB 日本宇部
生產企業:泰國宇部
規格用途
規格級別 | 其它 其它 其它 | 外觀顏色 | |
該料用途 | |||
備注說明 | 特性:標準強度純透明高用期 |
技術參數
性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
基本性能 | 成型收縮率 | UBEmethod | 1.4 | % | |
成型收縮率 | UBEmethod | 1.2 | % | ||
吸水率 | ASTM D-570 | 1.8 | % | ||
吸水率 | ASTM D-570 | 10.7 | % | ||
物理性能 | 比重 - | ASTM D-792 | 1.14 | ||
機械性能 | 抗沖擊強度 | -30° | ASTM D-256 | 3.0 | kgf.cm/cm |
彎曲彈性率 | 23° | ASTM D-790 | 8500 | kgf/cm2 | |
彎曲強度 | 80° | ASTM D-790 | 280 | kgf/cm2 | |
1%變形下的壓縮強度 | 23° | ASTM D-695 | 200 | kgf/cm2 | |
彎曲強度 | 80° | ASTM D-790 | 400 | kgf/cm2 | |
1%變形下的壓縮強度 | 23° | ASTM D-695 | 100 | kgf/cm2 | |
抗沖擊強度 | 23° | ASTM D-256 | 30 | kgf.cm/cm | |
TABER磨耗率 | ASTM D-1044 | 7 | mg | ||
硬度(洛氏、布氏) | 23° | ASTM D-785 | 55 | ||
彎曲強度 | -30° | ASTM D-790 | 1500 | kgf/cm2 | |
彎曲彈性率 | 23° | ASTM D-790 | 29000 | kgf/cm2 | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 120 | ||
彎曲彈性率 | -30° | ASTM D-790 | 35000 | kgf/cm2 | |
屈服下的伸張強度 | -30° | ASTM D-638 | 900 | kgf/cm2 | |
彎曲彈性率 | -30° | ASTM D-790 | 37000 | kgf/cm2 | |
屈服下的伸張強度 | 80° | ASTM D-638 | 440 | kgf/cm2 | |
屈服下的伸張強度 | 23° | ASTM D-638 | 800 | kgf/cm2 | |
擠剪強度 | 23° | ASTM D-732 | 600 | kgf/cm2 | |
硬度(洛氏、布氏) | 23° | ASTM D-785 | 85 | ||
彎曲強度 | 23° | ASTM D-790 | 1150 | kgf/cm2 | |
彎曲彈性率 | 80° | ASTM D-790 | 7500 | kgf/cm2 | |
彎曲強度 | -30° | ASTM D-790 | 1400 | kgf/cm2 | |
屈服下的伸張強度 | 23° | ASTM D-638 | 430 | kgf/cm2 | |
擠剪強度 | 23° | ASTM D-732 | 650 | kgf/cm2 | |
抗沖擊強度 | 23° | ASTM D-256 | 5.0 | kgf.cm/cm | |
彎曲彈性率 | 80° | ASTM D-790 | 4500 | kgf/cm2 | |
屈服下的延伸率 | 23° | ASTM D-638 | 7 | % | |
斷裂下的伸張強度 | 23° | ASTM D-638 | 780 | kgf/cm2 | |
彎曲強度 | 23° | ASTM D-790 | 410 | kgf/cm2 | |
斷裂下的延伸率 | 23° | ASTM D-638 | >200 | % | |
斷裂下的延伸率 | 23° | ASTM D-638 | 20 | % | |
屈服下的伸張強度 | -30° | ASTM D-638 | 1150 | kgf/cm2 | |
電氣性能 | 介電損耗 | 106HZ | ASTM D-150 | 0.12 | |
介電損耗 | 103HZ | ASTM D-150 | 0.10 | ||
介電常數 | 60HZ | ASTM D-150 | 3.9 | ||
介電損耗 | 60HZ | ASTM D-150 | 0.01 | ||
IEC電路 | UL746 | 600+ | V | ||
介電常數 | 106HZ | ASTM D-150 | 4.5 | ||
絕緣耐力 | ASTM D-149 | 20 | KV/mm | ||
介電損耗 | 106HZ | ASTM D-150 | 0.02 | ||
介電損耗 | 60HZ | ASTM D-150 | 0.10 | ||
介電常數 | 103HZ | ASTM D-150 | 3.8 | ||
屈服下的伸張強度 | kgf/cm2 | ASTM D-638 | 280 | 80° | |
介電常數 | 103HZ | ASTM D-150 | 8.0 | ||
體積電阻率 | ASTM D-257 | 1012 | Ω.cm | ||
體積電阻率 | ASTM D-257 | 1015 | Ω.cm | ||
介電損耗 | 103HZ | ASTM D-150 | 0.02 | ||
介電常數 | 106HZ | ASTM D-150 | 3.5 | ||
抗電弧強度 | ASTM D-495 | 119 | S | ||
介電常數 | 60HZ | ASTM D-150 | 9.0 | ||
熱性能 | 熔點 | DSC | 215-225 | °C | |
燃燒率 - | UL94 | V-2 | |||
熱變形溫度 | 4.6kgf/cm2 | ASTM D-648 | 195 | °C | |
線性熱膨脹系數 | ASTM D-696 | 8 | X的10-5cm/cm/°C | ||
熱變形溫度 | 18.6kgf/cm2 | ASTM D-648 | 75 | °C |
PA6 1013NB 日本宇部